電纜MY3*16+1*10礦用橡膠電纜MY4*16+1*10

額定電壓0.66/1.14KV及以礦用移動橡套軟電纜(GB12972.5-91)
本產品適用于額定電壓0.66/1.14KV及以下移動設備用銅芯橡皮護套軟電纜
主要用途
(MY)UY-0.38/0.66礦用移動橡套軟電纜
額定電壓為0.38/0.66KV各種井下移動采煤設備的電源連接
(MYP)UYP-0.38/0.66礦用移動屏蔽橡套軟電纜
額定電壓為0.38/0.66KV各種井下移動采煤設備的電源連接
(MYP)UYP-0.66/1.14礦用移動屏蔽橡軟套電纜
額定電壓為0.66/1.14KV各種井下移動采煤設備的電源連接
電纜MY3*16+1*10礦用橡膠電纜MY4*16+1*10芯數×導體 護套標稱厚度(mm)電纜外徑電纜參考重量(kg/km)
標稱截面(mm2)動力線芯UC-0.38/0.66UCP-0.38/0.66
動力線芯地線芯絕緣標稱厚度(mm)zui小值zui大值zui小值zui大值UCUCP
3×41×41.43.520.323.423.727.2670785
3×61×61.43.52326.426.430.1838927
3×101×101.6427.531.330.934.712921400
3×161×101.6429.633.43336.814651586
3×251×161.84.535.639.83943.221592296
3×351×161.84.538.742.142.146.325962783
3×501×162543.647.147.151.433853548
3×701×252549.754.452.457.142924477
芯數×導體 電纜外徑電纜參考重量(kg/km)
標稱截面(mm2)動力線芯護套標稱UC-0.38/0.66
動力線芯地線芯絕緣標稱厚度(mm)厚度(mm)zui小值zui大值
3×101×101.84.532.436.21476
3×161×101.84.534.638.41737
3×251×162541.445.32400
3×351×162544.248.42857
×3501×162.25.549.153.43549
3×701×252.25.555.560.24608
3×951×252.4661.265.94608
電纜絕緣主線芯之間及主線芯與地線之間的絕緣電阻,換算到+20℃時不低于100MΩ?km。
主線芯屏蔽層的過渡電阻換算到20℃時不高于3kΩ。
產品標準：MT818.5-1999。
MYP型電纜有3個帶絕緣屏蔽的主線芯和一個包覆半導電橡皮層的地線組成，圍繞半導電橡皮層墊芯絞合成纜。
外面擠包黑色氯化聚乙烯橡皮護套或黑色氯丁橡皮護套。
導電線芯：采用軟銅線，其性能符合 GB/T3956-1997。
絕緣：采用GB7594.2-1987中XJ-00A型橡皮。
線芯識別：采用絕緣分色識別，主線芯紅、綠、白。
地線：采用半導電橡皮包覆。
絕緣屏蔽：在絕緣表面包半導電帶。
成纜：3個主線芯1個地線圍繞半導電橡皮墊芯按右向絞合成纜。
護套：采用GB7594.7-1987中XH-03A型橡皮。護套橡皮的氧指數≥40。
成品電纜的阻燃性能滿足MT386-1995的要求。
電纜標志：電纜表面印有型號、電壓、規格及制造廠名稱。

電纜制造的基本工藝流程 
1．銅、鋁單絲拉制 
電線電纜常用的銅、鋁桿材，在常溫下，利用拉絲機通過一道或數道拉伸模具的模孔，使其截面減小、長度增加、強度提高。拉絲是各電線電纜公司的首道工序，拉絲的主要工藝參數是配模技術。 
2．單絲退火 
銅、鋁單絲在加熱到一定的溫度下，以再結晶的方式來提高單絲的韌性、降低單絲的強度，以符合電線電纜對導電線芯的要求。退火工序關鍵是杜絕銅絲的氧化. 
3．導體的絞制 
為了提高電線電纜的柔軟度，以便于敷設安裝，導電線芯采取多根單絲絞合而成。從導電線芯的絞合形式上，可分為規則絞合和非規則絞合。非規則絞合又分為束絞、同心復絞、特殊絞合等。 
為了減少導線的占用面積、縮小電纜的幾何尺寸，在絞合導體的同時采用緊壓形式，使普通圓形變異為半圓、扇形、瓦形和緊壓的圓形。此種導體主要應用在電力電纜上。 
4．絕緣擠出 
塑料電線電纜主要采用擠包實心型絕緣層，塑料絕緣擠出的主要技術要求： 
4．1．偏心度：擠出的絕緣厚度的偏差值是體現擠出工藝水平的重要標志，大多數的產品結構尺寸及其偏差值在標準中均有明確的規定。